Composition assisted tuning properties of CoCrxFe2-xO4 spinel nano ferrites

Résumé

Structural, magnetic properties, bandgap of sol gel auto-combustion synthesized single phase CoCrxFe2-xO4 (x = 0.0–1.0) nano ferrites, were studied by x-ray diffraction, vibration sample magnetometer, ultra violet visible spectroscopy. Linear decrease of lattice parameter with increasing Cr-content is ascribed to difference between ionic radii of Cr3+ (0.064 nm), Fe3+ (0.067 nm). Linear decrease of grain diameter with increasing Cr-content, shows presence of Cr in spinel lattice which hinders grain growth. Results show bandgap tenability; reveal that Cr-addition is effective in determining coercivity, saturation magnetization of studied samples. Results illustrate effectiveness of compositional variation for structural modification, leads to tuning of magnetic properties, bandgap.
Fichier non déposé

Dates et versions

hal-03821293 , version 1 (19-10-2022)

Licence

Copyright (Tous droits réservés)

Identifiants

Citer

P. Tiwari, S.N. Kane, Frédéric Mazaleyrat, U.P. Deshpande. Composition assisted tuning properties of CoCrxFe2-xO4 spinel nano ferrites. Materials Today: Proceedings, 2020, 32, pp.350-353. ⟨10.1016/j.matpr.2020.01.603⟩. ⟨hal-03821293⟩
28 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More